carbon black |
 |
carbon black |
 |
133-86-4 |
 |
rubber, foot wear, plastic, tyre |
 |
Product:N220 Iodine absorption number(g/kg):121±5 DBP absorption number(cm3/100g):114±5 CTAB surface area(cm2/g):106~116 Tint strength%:110~120 Heating loss(% ≤):1.5 Ash content%:0.5 Modulus at 300%(Mpa):-1.5±1.0
Product:N234 Iodine absorption number(g/kg):120±5 DBP absorption number(cm3/100g):125±5 CTAB surface area(cm2/g):114~124 Tint strength%:19~129 Heating loss(% ≤):1.5 Ash content%: 0.5 Modulus at 300%(Mpa): +0.5±1.0
Product:N326 Iodine absorption number(g/kg):82±5 DBP absorption number(cm3/100g):72±5 CTAB surface area(cm2/g):78~88 Tint strength%:107~117 Heating loss(% ≤):1.5 Ash content%:0.5 Modulus at 300%(Mpa):-3.0±1.0
Product:N330 Iodine absorption number(g/kg):82±5 DBP absorption number(cm3/100g):102±5 CTAB surface area(cm2/g):77~87 Tint strength%:98~108 Heating loss(% ≤) :1.5 Ash content%:0.5 Modulus at 300%(Mpa):-1.0±1.0
Product:N339 Iodine absorption number(g/kg):90±5 DBP absorption number(cm3/100g):120±5 CTAB surface area(cm2/g):88~98 Tint strength%:105~115 Heating loss(% ≤):1.5 Ash content%: 0.5 Modulus at 300%(Mpa): +0.5±1.0
Product:N375 Iodine absorption number(g/kg):90±5 DBP absorption number(cm3/100g):114±5 CTAB surface area(cm2/g):91~101 Tint strength% :110~120 Heating loss(%≤):1.5 Ash content%: 0.5 Modulus at 300%(Mpa):0.0±1.0
Product:N772 Iodine absorption number(g/kg):30±4 DBP absorption number(cm3/100g):65±4 CTAB surface area(cm2/g):29~37 Heating loss(% ≤):1.0 Ash content%:0.5 Modulus at 300%(Mpa):-5.8±1.0
Product:N660 Iodine absorption number(g/kg):36±4 DBP absorption number(cm3/100g):90±5 CTAB surface area(cm2/g):32~40 Heating loss(% ≤):1.0 Ash content%:0.5 Modulus at 300%(Mpa): -2.5±1.0
Product:N550 Iodine absorption number(g/kg):43±4 DBP absorption number(cm3/100g):121±5 CTAB surface area(cm2/g):38~46 Heating loss(% ≤):1.0 Ash content%: 0.5 Modulus at 300%(Mpa): -1.0±1.0
|
Industrial field |
plastic, polymer, resin, monomer, rubber & additives |
|
|
 |
|
|
|
 |
There are no existing companies to distribute selected chemical product |
|
 |
|
|